hardox 500 chemical composition

Hardox 500 Composition: Hardox 500 comprises low-carbon steel with a carbon content of not more than 0.25%. It also contains alloying elements such as chromium and nickel, intensifying its hardness, toughness, and strength. The percentage of chromium and nickel in Hardox 500 is 1.5% and 1%, respectively. General Product Description The bendable, weldable and highly abrasion-resistant steel. Hardox® 500 is a bendable and weldable abrasion-resistant steel with a nominal hardness of 500 HBW. Suitable for applications that demand higher wear resistance. Hardox® 500 increases payload and service life while maintaining good processability and toughness. General product Description The bendable, weldable and highly abrasion-resistant steel. Hardox 500 is a bendable and weldable abrasion-resistant steel, with a nominal hardness of 500 HBW. Suitable for applications that demand higher wear resistance. Hardox 500 is known as hard-to-cut steel possessing supreme abrasive wear resistance that makes it suitable for industrial applications especially for transportation. 0.25 0.25 0.005 Plate 0.30 0.70 1.60 0.020 0.010 1.50 0.005 The steel is grain refined. *) Intentional alloying elements. Carbon Equivalent CET (CEV) sheet 2.0 - 6.5 plate 4.0 - 13.0 plate 13.1 - 19.9 plate 0.33 (0.45) Delivery Conditions The delivery condition is Q or QT (Quenched or Quenched and Tempered). Hardox 500 is an abrasion resistant plate with a hardness of 500 HBW, intended for applications where demands are imposed on ab ra si on re sistance. Applications. Chemical Composition. (ladle analysis) Crushers, sieves, feeders, measuring pockets, skips, cutting edges, conveyors, buckets, knives, gears, sprockets, etc. Plate C Si Mn P S Cr Ni ... There are two types of 500 BHN PLATE (HARDOX 500) available, rolled plates and quenched plates. The rolled plates range from 3 mm to 200 mm, while the quenched plates have a thickness of up to 40 mm. Both types come in various widths up to 4000 mm. The main difference between the two types is that the quenched plate undergoes additional heat ... Schlam knows that it can, with a boost in loading capacity of up to 20%. You too can protect your investments with Hardox ® 500 Tuf in mining haul truck bodies. It has a guaranteed narrow Brinell hardness range of 475-505 HBW, an impact energy of 27 J at -20°C (20 ft-lb at -4°F) and a typical value of 45 J at -40°C (33 ft-lb at -40°F ... Welding of Hardox 400, 450, 500, 550 and 600. Low alloy or carbon steel base welding consumables having a maximum yield strength of MPa (72 ksi) are generally recommended for Hardox 400, 450, 500, 550 and 600. Higher strength welding filler materials (having a maximum yield strength of 900 MPa (130 ksi) can be used for Hardox 400 and 450 in the ... 450 – 540. Brinell hardness (HBW) is tested in SSAB laboratories in accordance with EN ISO 6506-1. The control is carried out at least once per 40 tons of products. Hardox sheet steel has a hardness of 450-540 HBW Brinell, which corresponds to 47-54 HRC Rockwell. For comparison, bearing hardness starts at 55 HRC. Hardox® 450 is probably the world’s most recognized wear-resistant steel, with tight tolerances and excellent structural properties, only from SSAB. With a nominal hardness of 450 HBW, Hardox® 450 combines good bendability and excellent weldability. The extra 50 HBW hardness over our Hardox® 400 grade provides better dent and abrasion ... The real chemical composition of Hardox Extreme for a 10 mm thick plate is shown Table 1. The analyzed material belongs to the medium carbon steel group (0.44% C). Attention should be drawn to the contents of such elements as: chromium (0.83%), nickel (2.01%) and molybdenum (0.14%) which intensify the influence of boron, whose content is 0.0021%.